Fire Resistant Plastic Injection Molding Products , 110mm Oyster White Plastic Reducer
Plastic Reducer Injection Molding part is a special design for gear that is used to home appliances , plastic reducer is made from POM that is one of engineering materials with perfect insulation .
Plastic injection molding reducer has a threaded hole end with fixing clip beams that supports threaded rod or screw to secure pieces .
Material for Plastic Reducer for Gear Injection Molding
POM (Polarizing Optical Microscope )
Specification for Plastic Reducer for Gear Injection Molding
Length : 95 mm
Diameter : 18 mm
Threaded diameter : M8
Note : this reducer for gear injection molding part is customized according to special construction .
Tolerances for Plastic Reducer for Gear Injection Molding
1 , all are in mm and based on “ + “ “ –”tolerance
2 , for unspecified tolerance , based on ISO 2768-m with grade MT 7
Mechanical Property for Plastic Reducer for Gear Injection Molding
|Tensile strength MPa||70|
|Elongation at break %||40|
|Bending strength MPa||90|
|Modulus of elasticity for tension MPa||3160|
|modulus of elasticity for bending MPa||2880|
|Compressive strength MPa||127|
|Shearing strength MPa||67|
|Notched Impact Strength(J/m)||76|
Thermal Performance for Plastic Reducer for Gear Injection Molding
|Heat distortion Temperature(1.82MPa)℃||110|
|Normal working temperature ℃||80|
|Working temperature arrange ℃||-40℃～90℃|
|Coefficient of linear expansion (×10K)||7.5|
|Heat conduction W/(m·K)||0.23|
Physical Performance for Plastic Reducer for Gear Injection Molding
|Specific volume resistance Ω·cm||10|
|Specific inductive capacity(10Hz)||3.8|
|Dielectric loss tangent (10Hz)||0.005|
Notes for Plastic Reducer for Gear Injection Molding
POM plastic Reducer Injection Molding part are easy to be cracked and pulverized outside long-term .
Don’t put POM plastic Reducer Injection Molding parts under temperature over 100℃
Don’t put POM plastic Reducer Injection Molding parts under circumstance with alkali and oxidant .